Abstract
This study investigated the segmental dynamics of polymers near polymer-polymer interfaces by probing the rotation of polymer-tethered fluorescent molecules using imaging rotational fluorescence correlation microscopy. Multilayered films were utilized to provide spatial selectivity relative to different polymer-polymer interfaces. In the experimental setup, for the overlayer polymer, polystyrene (PS) was employed and a 15 nm-thick probe-containing layer was placed ≈25nm apart from different underlayer polymers with glass transition temperatures (Tg) either lower or higher than that of PS. The underlayer of poly-n-butyl methacrylate had 72K lower Tg than that of PS, whereas polymethyl methacrylate and polysulfone had 22 and 81K higher Tg, respectively, than that of PS. Two key dynamic features of the glass transition, the non-Arrhenius temperature dependence and stretched relaxation, were examined to study the influence of soft and hard confinements on the segmental dynamics of the overlayer polymer near the polymer-polymer interfaces. Although complications exist in the probing location owing to the diffusion of the polymer-tethered probe during the annealing protocol to consolidate the multilayers, the results suggest that either the segmental dynamics of the polymer near the polymer-polymer interface do not change owing to the soft and hard confinements or the interfacial perturbation is very short ranged.
Published Version (
Free)
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.