Abstract
Abstract Directional solidification of nickel-base superalloy components for gas turbine rotor blades offers a significant improvement in creep strength while at the same time yielding an anisotropic, heterogeneous microstructure. In such a material, some of the continuum assumptions of linear elastic fracture mechanics begin to break down, and local (microscopic) conditions can lead to significant deviation in fatigue crack growth rate from the global (macroscopic) trend. Fatigue crack life prediction for a large population of fielded components requires a probabilistic treatment of the material fatigue crack growth behavior. A common approach to probabilistic fatigue crack life prediction involves sampling the Paris law coefficients from a large number of crack growth experiments, which can lead to effectively “smoothing” the local intraspecimen variability out of the model. The length scale of variability is discussed as it relates to material microstructure and crack life prediction. Results from fatigue crack growth experiments on a directionally solidified superalloy are presented and spatial variation in the fatigue crack growth rate is examined. Periodicity of the crack growth rate variation is compared with the scale of microstructural heterogeneity.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.