Abstract
The study of mechanical response of materials at small length scales has gained importance due to the recent advances in micro- and nano-fabrication as well as testing systems. However, most of the reported work has been dedicated to investigate single-crystals or boundary-containing metallic systems, while much less attention has been paid to composite materials, and in particular those combining soft and hard phases. In this work, a systematic procedure is followed for machining micropillars of diameters ranging from 1 to 4μm in a WC-Co composite with a WC mean grain size around 1μm, by means of focused ion beam milling. In-situ uniaxial compression of the micropillars and subsequent field emission scanning electron microscopy inspection were conducted. Clear size effects are evidenced. Smaller test specimens (probe size approaching the mean WC size) exhibit deformation/failure mechanisms observed for WC crystals; while for bigger sample sizes, the mechanical response involves several mechanisms directly linked with the microstructural characteristics of the bulk-like cemented carbide material. On the other hand, independent of micropillar size, carbide-carbide or carbide-binder interfaces are found to be preferential sites for nucleation of critical damage events.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: International Journal of Refractory Metals and Hard Materials
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.