Scaffold design for artificial tissue with bone marrow stem cells

Abstract

ObjectiveThe aim of this study was to test polymeric materials (collagen, fibrin, polyimide film, and polylactic acid) for single- and multi-layer scaffold formation. Materials and methodsIn our study, we used rabbit bone marrow stem cells (rBMSCs) and human mesenchymal stem cells (hMSCs) with materials of a different origin for the formation of an artificial scaffold, such as a collagen scaffold, fibrin scaffold produced from clotted rabbit plasma, electrospun poly(lactic acid) (PLA) mats, polyimide film (PI), and the combination of the latter two. Cell imaging was performed 3–14 days after cell cultivation in the scaffolds. Time-lapse imaging was used to determine hMSC mobility on the PI film. ResultsCell incorporation in collagen and clotted fibrin scaffolds was evaluated after 2-week cultivation in vitro. Histological analysis showed that cells penetrated only external layers of the collagen scaffold, while the fibrin clot was populated with rBMSCs through the entire scaffold thickness. As well, cell behavior on the laser micro-structured PI film was analyzed. The mobility of hMSCs on the smooth PI film and the micro-machined surface was 20±2μm/h and 18±4μm/h, respectively. After 3-day cultivation, hMSCs were capable of spreading through the whole 100±10μm-thick layer of the electrospun PLA scaffold and demonstrated that the multilayer scaffold composed of PI and PLA materials ensured a suitable environment for cell growth. ConclusionsThe obtained results suggest that electrospinning technology and femtosecond laser micro-structuring could be employed for the development of multi-layer scaffolds. Different biopolymers, such as PLA, fibrin, and collagen, could be used as appropriate environments for cell inhabitation and as an inner layer of the multi-layer scaffold. PI could be suitable as a barrier blocking cell migration from the scaffold. However, additional studies are needed to determine optimal parameters of inner and outer scaffold layers.