Abstract
Surfactant mediated growth of strained InAs/AlAs0.56Sb0.44 quantum wells on InP (001) substrate is investigated. X ray diffraction and transmission electron microscopy analysis reveal that the supply of antimony on InAs surface delays the 2D to 3D growth transition and allows the growth of thick InAs/AlAsSb quantum wells. Quantum well as thick as 7 ML, without defect was achieved by Sb surfactant mediated growth. Further high resolution transmission electron microscopy measurement and geometric phase analysis show that InAs/AlAsSb interfaces are not abrupt. At InAs on AlAsSb interface, the formation of a layer presenting lattice parameter lower than InP leads to a tensile stress. From energetic consideration, the formation of As rich AlAsSb layer at interface is deduced. At AlAsSb on InAs interface, a compressive layer is formed. The impact on optical properties and the chemical composition of this layer are discussed from microscopic analysis and photoluminescence experiments.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.