Abstract
An experimental assessment was conducted of the silicon carbide (SiC) cladding oxidation rate in steam under conditions that are representative of loss-of-coolant accidents in light water reactors (LWRs). SiC oxidation tests were performed with monolithic alpha-phase tubular samples at atmospheric pressure for steam temperatures of 1140°C and 1500°C and a Reynolds number range of 40 to 330. Linear weight loss of SiC samples due to boundary layer controlled reaction of silica scale (SiO2 volatilization) was experimentally observed. The weight loss rate increased with increasing steam flow rate and temperature. Over the range of test conditions, SiC oxidation rates were shown to be about three orders of magnitude lower than the oxidation rates of Zircaloy-4. This underlines a weaker interplay between oxidation and mechanical property degradation in comparison with Zircaloy. SiC volatilization correlations for developing laminar flow in a vertical channel were formulated for LWR accident modeling.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.