Abstract
Stress corrosion cracking (SCC) in the fusion boundary (FB) region of an Alloy 182-low alloy steel (LAS) dissimilar weld joint in 288 °C water was investigated by experiments and finite element simulation. Creviced bent beam and crack growth rate (CGR) experiments showed that, while the FB was a barrier to SCC growth, further crack growth into LAS was activated by a combined effect of sulfate and dissolved oxygen in water. Finite element simulation suggested that a positive gradient of hardness as the crack approached to the FB in dilution zone caused decreased CGR. Role of microstructure and water chemistry in SCC was discussed.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.