Abstract
Polylactic acid (PLA) has been modified by electron beam radiation in the presence of glycidyl methacrylate (GMA) to enhance the melt strength of PLA. The modified PLA was prepared by varying both the amount of GMA and the irradiation dose and was characterized by observing the thermal properties, the melt viscoelastic properties and the gel fraction. For comparison, virgin PLA was also irradiated. All irradiated virgin PLA had a lower complex viscosity and a storage modulus compared to virgin PLA due to irradiation-induced chain scission. However, these properties were remarkably improved due to formation of long chain branching and retarding chain scission if GMA was introduced in this system. The increase in melt viscoelastic property was much dependent on the irradiation dose. At optimum doses of radiation, it showed maximum complex viscosity and storage modulus. The PLA irradiated with 20 kGy in the presence of 3 phr GMA showed a complex viscosity of about 10 times higher and a storage modulus of 100 times higher than those of virgin PLA at 0.1 rad/s. Gel fraction measurement revealed that chain scission and branching was more dominant than crosslinking. The biodegradability of irradiated PLA was slightly decreased by the presence of GMA.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.