Reverse micelle synthesis of oxide nanopowders: Mechanisms of precipitate formation and agglomeration effects

Abstract

We present an analysis of reverse micelle stability in four model systems. The first two systems, composed of unstable microemulsions of isooctane, water, and Na-AOT with additions of either iron sulfate or yttrium nitrate, were used for the synthesis of iron oxide or yttrium oxide powders. These oxide powders were of nanocrystalline character, but with some level of agglomeration that was dependent on calcination temperature and cleaning procedures. Results show that even though the reverse micellar solutions were unstable, nanocrystalline powders with very low levels of agglomeration could be obtained. This effect can be attributed to the protective action of the surfactant on the surfaces of the powders that prevents neck formation until after all the surfactant has volatilized. A striking feature of the IR spectra collected on the iron oxide powders is the absence of peaks in the ∼1715cm−1 to 1750cm−1 region, where absorption due to the symmetric CO (carbonyl) stretching occurs. The lack of such peaks strongly suggests the carbonyl group is no longer free, but is actively participating in the surfactant-precipitate interaction. The final two microemulsion systems, containing CTAB as the surfactant, showed that loss of control of the reverse micelle synthesis process can easily occur when the amount of salt in the water domains exceeds a critical concentration. Both model systems eventually resulted in agglomerated powders of broad size distributions or particles that were large compared to the sizes of the reverse micelles, consistent with the notion that the microemulsions were not stable and the powders were precipitated in an uncontrolled fashion. This has implications for the synthesis of nanopowders by reverse micelle synthesis and provides a benchmark for process control if powders of the highest quality are desired.