Abstract
Through methods, such as microscope analysis, metallographic examination, the crack located nearby the fusion line between tee joint and outlet steam pipe of subcritical power station boiler final superheater header is reheat crack (the main crack occurred in the heat affected zone and extended along the fusion line and grain boundary in HAZ. There are many small cracks paralleling with main crack). The base metal material (12Cr1MoV) and excessive welding residual stress are the primary inducement of crack. In repair crack, the measures of reducing residual stress, such as lower welding heat input, reducing thickness of welding layer, hammer blowing, assigning reasonably heat treatment power ,lengthening holding time and so on, were taken. The welding repair succeeded greatly.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.