Abstract
Iron nanowires were successfully prepared by electrodeposition method via ordered nanoporous anodized aluminum oxide (AAO) template since the technique is simple and cost-effective. The preparation of nano porous anodized aluminum template involved annealing and electropolishing as a pretreatment. It has been found that regularity of pores increases after the pre-treatment. The average surface roughness factor (Ra) was measured with the help of portable surface roughness tester. Pore diameter, pore density, porosity and uniformity of pores was determined with the help of image-J software. Morphology of nanoporous oxide and iron nanowires was confirmed with FE-SEM and EDS analysis. The pore diameter of template ranged from 105 nm to 120 nm. The fabricated nano wires were found to have length of 643 nm and diameter of 103 nm with unique environmental applications.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.