Abstract
During the development of YBa2Cu3O7−δ (YBCO) coatings on flexible metal tapes, it has become evident that the achievable critical current (Ic) reaches a maximum value of about 200 A per cm of conductor width at a coating thickness of 1–2 μm. Additional YBCO beyond this thickness can actually reduce Ic. To investigate, critical current density (Jc) has been measured for samples with YBCO ranging from 0.39 to 6.3 μm in thickness. Several films were thinned by ion milling and remeasured with two significant results: almost no supercurrent is carried at thickness levels above 2 μm; and for films thicker than 3 μm, Jc is drastically reduced near the substrate as well.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.