Abstract
About 25 % of iron oxides in the sintering process are wastes. In this paper, sintered waste (SW) was used as a source of iron oxides to prepare both hard and soft magnetic glass-ceramics via a melting-quenching technique. About 71 % by wt. of sintered waste was used for preparing soft magnetic glass-ceramics, while ∼46 % was used for preparing hard magnetic glass-ceramics. The comparison between ferrimagnetic glass-ceramics prepared from pure chemicals and that from sintered waste before and after heat treatment was studied. X-ray diffraction shows crystallization of both hematite and Zn-ferrite phases in sintered waste while pure Zn-ferrite or Ba-hexaferrite phases were crystallized in soft magnetic and hard magnetic glass-ceramics, prepared from sintered waste, respectively. Transmission electron microscopy determined the crystalliza- tion of nano-particles ∼20 nm and <15 nm for soft and hard magnetic glass-ceramics respectively. Vibrating scanning magnetometry revealed a significant increase in saturation magnetization from ∼26 emu/g for sintered waste to ∼44 emu/g in soft magnetic glass ceramics while it decreased to ∼12 emu/g for hard magnetic glass-ceramics.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.