Abstract
AbstractComposites of recycled carbon fiber (CF) with up to 30 wt % loading with polyethylene (PE) were prepared via melt compounding. The morphology of the composites and the degree of dispersion of the CF in the PE matrix was examined using scanning electron microscopy, and revealed the CF to be highly dispersed at all loadings and strong interfacial adhesion to exist between the CF and PE. Raman and FTIR spectroscopy were used to characterize the surface chemistry and potential bonding sites of recycled CF. Both the Young's modulus and ultimate tensile stress increased with increasing CF loading, but the percentage stress at break was unchanged up to 5 wt % loading, then decreased with further successive addition of CF. The effect of CF on the elastic modulus of PE was examined using the Halpin‐Tsai and modified Cox models, the former giving a better fit with the values determined experimentally. The electrical conductivity of the PE matrix was enhanced by about 11 orders of magnitude on addition of recycled CF with a percolation threshold of 7 and 15 wt % for 500‐μm and 3‐mm thick samples. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci, 2008
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.