Abstract
Magnetic recording pigment of Fe 4 N particles was prepared by nitrogenizing acicular metal iron powder. The treatment to obtain stoichiometric Fe 4 N was carried out at 400°C for 3 hours in NH 3 -H 2 (3:1) mixed gas. The saturation magnetization and coercive force were 120 emu/g and 700 Oe respectively. The Curie point of the powder coincided well with that of bulk material. Test tapes were prepared with this Fe 4 N powder. The remanent magnetic flux density (Br) of the tape was 2200 G and the coercive force was 670 Oe. From test immersion in saline solution, it is confirmed that the chemical stability of the Fe 4 N tape is superior to the Fe 4 N tape is superior to the metal tape.