Abstract

This study examines atomic diffusion bonding (ADB) of wafers using Ag and Au films in vacuum at room temperature. Transmission electron microscopic images show remarkable crystal lattice rearrangement that occurs at depths greater than 50 nm from the connected Ag/Ag film interface. The Au/Au interface fluctuation attributable to the crystal lattice rearrangement is 5–10 nm. X-ray diffraction reveals that the crystal lattice rearrangement for Ag/Ag interface occurs remarkably at thicknesses of less than 150 nm, indicating high bonding potential when using Ag films in ADB. Large surface roughness in the thick film region probably suppresses the crystal lattice rearrangement.

Full Text
Paper version not known

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.