Abstract
Reactivity of several oxide materials (OM) with BSCCO powder and oxygen diffusion through OM layer has been tested at temperature ≈840 °C in air. The OM (e.g.: BaZrO 3, SrCO 3, MgO and ZrO 2) showing the low or no reactivity with BSCCO have been mixed (10 wt.%) with precursor powder and used for single-core tapes. Bi-2223/Ag/OM/Ag single-core tapes with oxide barriers made of BaZrO 3, SrCO 3, ZrO 2 and Al 2O 3 have been also prepared by a standard powder-in-tube technique. The used OM in the direct contact with BSCCO influences the electrical properties of Bi-2223 phase differently. These is because the oxides react with BSCCO during the heat treatment and simultaneously affect the 2212→2223 phase transformation, the Bi-2223 grain growth and so also grain connectivity. SrCO 3 powder has been evaluated as the best material from the point of no destructive effect on 2223 phase transport current property. The oxide barrier controls the oxygen diffusion during the tape heat treatment and simultaneously the HTS phase formation kinetics, its purity and content within the superconducting core. For single-core Bi-2223/Ag/OM/Ag tapes, the highest current density was measured for Al 2O 3 due to only slightly reduced oxygen diffusion through the barrier.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.