Abstract
A combination of both conventional and advanced high-resolution characterization techniques was applied to study the modified layers on the surface of three composite Al-Cr arc cathodes with identical nominal composition of Al-50 at.% Cr but varying powder grain sizes. The results revealed that the modified layers consist mainly of metastable phases such as Cr solid solution, high temperature cubic Al8Cr5, supersaturated Al solid solution, and icosahedral quasicrystal. The metastable phase formation indicates that high cooling rates were involved during the solidification of molten material produced in the arc craters during cathode spot events. The average cooling rate was estimated to be 106 K/s based on secondary dendrite arm spacing measurements and supporting phase-field based simulations. The formation mechanisms of the modified layers are discussed based on the obtained results and the current literature.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.