Abstract
The behavior of radiation-induced segregation (RIS) and intergranular corrosion at random grain boundaries and Σ3 coincidence site lattice (CSL) boundaries in proton-irradiated 316L stainless steel was examined. The frequency of the CSL boundaries was enhanced up to 86.6% by grain boundary engineering treatment prior to irradiation. Significant nickel enrichment and chromium depletion were induced at the random grain boundary owing to the RIS. At faceted Σ3 CSL boundaries, chromium depletion occurred at the asymmetrical boundary facet plane whereas no RIS was observed at the coherent twin boundary. After the electrochemical etching test, an intergranular corrosion groove was found along the random grain boundaries because of the low chromium concentration (∼12%) at the boundaries. At the faceted Σ3 CSL boundaries, the discontinuous groove along the asymmetric facet plane was completely disrupted by the non-corrosive coherent twin boundary.
Sign-in/Register to access full text options 
Free) 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call