Abstract
Nano- and micro-indentation studies were carried out to characterise a plasticity mechanism through the evolution of localised shear bands that drive material's deformation at sub-micron length scale. Initial deformation of Zr-based bulk metallic glass (BMG) was investigated with nanoindentation tests using a spherical indenter. The indentation cycle reflects an elastic deformation with the yielding load of approx. 3 mN. For designed cycling indentation, hardening and softening phenomena were observed in nano- and micro-indentations, respectively. High-precision dynamic mechanical relaxation measurements were performed using a Dynamic Mechanical Analyzer (DMA), on decreasing frequency from 160 Hz to 0.1 Hz. A mechanical response of the BMG surface to a concentrated impact load was also studied. The obtained results indicated that the studied Zr-based BMG behaved as an elastic-perfectly plastic material at macroscale with discrete plasticity events at smaller length scales.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have