Abstract
ABSTRACTThis paper reports experimental observations that show non‐irradiated Gilsocarbon polygranular nuclear graphite fits within the quasi‐brittle class of materials. Such materials exhibit a degree of damage tolerance that depends on the stability of cracks that nucleate in the microstructure. Modelling efforts to predict the influence of microstructure on damage tolerance require direct observation of crack nucleation and growth to support them.Here, the technique of digital image correlation was applied to optical observations to measure the full field distribution of displacements on the surface of large (>100 mm dimension) specimens, loaded in uniaxial flexure. Repeated cyclic loading to strains approaching failure results in an inelastic (i.e. non‐recoverable) strain, and a decrease in the static elastic modulus. Digital image correlation was also used for early detection and characterisation of fracture nuclei (short cracks). Such short cracks show a stable propagation stage before causing catastrophic failure. The displacement fields were used to calculate directly the energy release rate of the short cracks via a contour integral method. The value is consistent with the critical strain energy release rate for unstable fracture obtained from standard mode I fracture tests.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Fatigue & Fracture of Engineering Materials & Structures
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.