Abstract
Material strength is dependent on several factors, including precipitation strengthening, which is the main strengthening mechanism in AA7050 aluminum alloys. These alloys contain numerous nanometer-scale precipitates that occur throughout grains and along grain boundaries when subjected to a range of heat treatment conditions. In this study, three different characterization methods were used to characterize these nanoscale precipitates: conventional scanning transmission electron microscopy (STEM); laboratory-based small-angle X-ray scattering (SAXS); and a new software analysis tool developed by Thermo Fisher Scientific: automated particle workflow (APW). Each method was used to determine average precipitate size and volume fraction of precipitation in AA7050-T7451 specimens with variable post-T7 heat treatment procedures. STEM techniques measured the average particle size as ranging from 7.6 to 17.6 nm, compared to 6.3–10.7 nm for SAXS, and 7.4–10.8 nm for APW. Volume fraction determinations varied from 0.23 to 16 %, depending on method, and were the most difficult to quantify. Significant outcomes of the current study are that SAXS and APW are the most accurate methods for determining average particle size and that future work is needed to effectively analyze precipitate volume fraction.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call