Abstract
In this paper, an effective annealing method in which CdMnTe:In (CMT:In) single crystals were coated with CMT powders of the same composition was used to improve the crystal quality of CMT:In crystals. The results indicated that the density of Te inclusions decreased as the annealing time increased. The resistivity and IR transmittance of annealed CMT:In crystals were enhanced obviously. The resistivity of 120h annealed crystal increased even two orders of magnitude. The reduction of full-width at-half-maximum (FWHM) and the increase of the intensity of X-ray rocking curve indicated an improvement of the crystal quality. PL measurements also showed the crystal quality improved after annealing. No characteristic peak of 241Am γ-ray could be observed in the detector fabricated with as-grown crystal. Remarkably, for the detector fabricated with annealed crystals, the peak of 241Am γ-ray appeared. And the energy resolution and μτ value were improved as the annealing time increased. Specially, 120h annealed CMT:In crystal with 10.11% energy resolution and 1.20×10−3cm2/V μτ value has the best detector performance.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call