Purification of nickel solution obtained from leaching of Ni–Mo ore by chemical precipitation

Abstract

Purification of nickel solution obtained from leaching of Ni–Mo ore by chemical precipitation is described in this paper. The impurities Fe3+, Cu2+, Ca2+ and Mg2+ were separated from nickel solution by the methods of jarosite, hydrolysis, sulphide and fluoride precipitation. The optimum conditions were obtained as follows: For Fe removal, sodium jarosite seeding 1 g L−1, reaction temperature 95°C, retention time 30 min, initial pH of the solution 1·8 and hydrolysis precipitation at pH 4·2 for 30 min; For Cu removal, 1·6 times the stoichiometric amount NiS, reaction temperature 80°C and duration 30 min. Under the optimum conditions, it was found that the concentrations of Fe, Cu, Ca and Mg could be reduced to 3·6, 1·8 mg L−1, 0·1 and 0·2 mg L−1 respectively. The total recovery of nickel was beyond 98%.Dans cet article, on décrit la purification de la solution de nickel obtenue à partir du lessivage du minerai de Ni-Mo par précipitation chimique. On a séparé les impuretés de Fe3+, Cu2+, Ca2+ et Mg2+ de la solution de nickel par les méthodes d’hydrolyse de la jarosite et de précipitation du sulfure et du fluorure. On a obtenu les conditions optimales comme ceci: pour l’enlèvement du Fe, ensemencement de 1 g L−1 de jarosite de sodium, température de réaction de 95°C, temps de rétention de 30 min, pH initial de la solution de 1·8 et précipitation par hydrolyse à un pH de 4·2 pendant 30 min; pour l’enlèvement du Cu, 1·6 fois la quantité stœchiométrique de NiS, température de réaction de 80°C et durée de 30 min. En conditions optimales, on a trouvé qu’on pouvait réduire les concentrations de Fe, Cu, Ca et Mg à 3·6, 1·8, 0·1 et 0·2 mg L−1 respectivement. La récupération totale du nickel était au-delà de 98%.