Abstract
Room temperature vulcanized (RTV) silicone rubber composites reinforced by multi-walled carbon nanotubes (MWCNTs) were prepared. The effect of surface modification methods and MWCNT contents on the properties of the RTV silicone rubber composites was investigated. The properties of the composites were improved when the treated MWCNTs were used. After treated by polyester-modified polydimethylsiloxane solution (BKY-310), the MWCNTs were uniformly dispersed in the silicone rubber matrix. When 5 phr of MWCNTs was added, the composite achieved good comprehensive performance. Its tensile strength, tear strength, elongation and onset decomposition temperature reach 2.0 MPa, 11.7 kN/m, 238% and 510 °C, respectively. But the above said values for the composite with untreated MWCNTs are only 1.1 MPa, 7.0 kN/m, 83% and 484 °C, respectively.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.