Abstract
Recent progresses in R&D of the TFA-MOD process for coated conductors are reviewed. On the efforts for high Ic tapes, the new process to prevent the crack formation in the thick film, which is the intermediate annealing between the calcination and the crystallization steps, was developed. Additionally, control of the starting composition, especially for the Ba-poor composition from the Y:Ba:Cu=1:2:3 stoichiometric one, is found to be effective to improve the Jc value of the films. Consequently, the extremely high Ic value of 735A was obtained. On the other hand, a reel-to-reel system has been applied to fabricate long tapes. A reasonable long tape of 25m with 100A was obtained by the increase of the gas flow rate which assists to enhance the conversion reaction rate. Additionally, it was found that the rigorous humidity control in the coating chamber is important to obtain the uniform characteristics in long tapes. The idea was applied to fabricate long tapes and a 56m tape with the end-to-end Ic value of 250A was realized.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.