Produit de solubilité apparent de la fluorapatite frittée

Abstract

Solubility of sintered fluorapatite. The apparent solubility of fluorapatite (Fap) sintered at 890°C for one hour under an argon atmosphere was determined at 25, 30, 37 and 50°C in dilute solutions of phosphoric acid of various concentrations. The Fap displayed retrograde solubility. When the concentration of H3PO4 was below 20.10−3 mol/L, infrared spectroscopy and X-ray diffraction patterns did not show any significant evolution of the solid after equilibration. For a concentration of 50. 10−3 mol/L, the apatite phase was modified with formation of calcium fluoride and of an amorphous phosphated phase CaHP04. Scanning electron microscopy showed a grain growth when temperature increased. The evolution towards new phases was assigned to secondary reactions and to the surface effect of the solid particles. Le produit de solubilité apparent de la fluorapatite (Fap), frittée à 890°C pendant une heure sous atmosphère d'argon, a été déterminé à 25, 30, 37 et 50°C, dans des solutions diluées d'acide phosphorique de concentration variant de 5.10−3 à 50.10−3 mol/L. Les résultats obtenue montrent que la Fap frittée présente une solubilité rétrograde. L'analyse par spectroscopie infrarouge et diffraction des rayons X du solide en équilibre avec la solution montre que celui-ci ne subit pas d'évolution significative jusqu'à la concentration en H3PO4 de 20.10−3 mol/L. Pour la concentration de 50.10−3 mol/L, on note une modification de la phase apatitique avec formation de fluorine et d'une phase phosphatée amorphe CaHP04. L'examen par microscopie électronique à balayage a permis de mettre en évidence un grossissement des grains en fonction de la température. L'évolution de l'apatite a été attribuée à des réactions secondaires faisant intervenir les entités chimiques en solution, et à l'effet de surface des particules solides.