Abstract
Copper (Cu) matrix composites reinforced with 0.2, 5 and 10vol% single wall carbon nanotubes (SWCNT) and 5 and 10vol% multi-wall carbon nanotubes (MWCNT) were processed by high energy milling of pure copper powder with carbon nanotubes (CNTs) and subsequent consolidation by vacuum hot pressing. Microstructural observations of the sintered composites revealed equiaxed twinned microstructure for 0.2vol% SWCNT composite and elongated grain structure, with CNT layers in between, in composites having higher CNTs content. The porosity in the composites was associated with CNT layers. The distribution of CNTs was found to be different in axial and transverse directions. Significant improvement in hardness of Cu–SWCNT composite was observed with increase in CNTs content. Whereas, in case of MWCNT composite, hardness reduced for 10vol% CNT composites. Compression strength of the SWCNT samples was found to be higher than the MWCNT reinforced samples.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.