Abstract
ABSTRACTIn this work multi-component equiatomic and non-equiatomic AlCoCrCuFeTix hexanary high-entropy alloys (HEA) was synthesised through mechanical alloying. The prepared powder was sintered via spark plasma sintering. Influence of alloying element variation in the multi-component system was studied in terms of phase formation and crystal structure by using Thermo-Calc and X-ray diffraction characterization technique (XRD). Particle morphology and chemical analysis studies were carried out through scanning electron microscopy along with Electron Dispersive X-ray Spectroscopy. The crystal structure and nano crystallinity of the hexanary system were recognised using transmission electron microscope (TEM and Selected Area Electron Diffraction [SAED]) while the formation of a solid solution was also studied and discussed. From the XRD and TEM characterisation of 20 h in, milled powders and sintered samples, it was confirmed that the developed HEA system forms a single solid solution BCC phase. The sintered alloy exhibits 97% relative density and an average hardness of 590 VHN.Special theme block on high entropy alloys, guest edited by Paula Alvaredo Olmos, Universidad Carlos III de Madrid, Spain, and Sheng Guo, Chalmers University, Gothenburg, Sweden.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.