Microstructures and properties of CoCrCuFeNiMox high-entropy alloys fabricated by mechanical alloying and spark plasma sintering

Abstract

ABSTRACTCoCrCuFeNiMox (x values in molar ratio, x = 0, 0.2, 0.4 and 0.8) high-entropy alloys were prepared by mechanical alloying and spark plasma sintering method. The effects of Mo addition on microstructure and mechanical properties were investigated. The X-ray diffraction (XRD) result showed that the addition of Mo into CoCrCuFeNi high-entropy alloy (HEA) changed the original phase constitution from FCC to FCC + σ + μ and the peak intensity of (1 1 1) shifted to the left and decreased steadily. The field emission scanning electron microscope confirmed that the Cu-rich second FCC phase disappeared and the σ phase with a tetragonal structure expanded as the Mo content was increased. Additionally, a high density of dimple-like features were seen in CoCrCuFeNi HEA while typical quasi-cleavage facets could be observed from the fracture surfaces of the HEAs with the addition of Mo. The Mo0.8 alloy showed a good wear resistant and appropriate strength with fracture strain 22.70%, fraction coefficient 0.65, hardness 530 HV and compressive strength 1448 MPa.Special theme block on high entropy alloys, guest edited by Paula Alvaredo Olmos, Universidad Carlos III de Madrid, Spain, and Sheng Guo, Chalmers University, Gothenburg, Sweden.