Probing Long- and Short-Range Disorder in Y2Ti2–xHfxO7 by Diffraction and Spectroscopy Techniques

Abstract

We studied the long-range average and short-range local structures in Y2Ti2–xHfxO7 (x = 0–2.0) using diffraction and spectroscopy techniques, respectively. Both neutron and synchrotron X-ray powder diffraction data show a clear phase transition of the average structure from ordered pyrochlore to disordered defect-fluorite at x ≈ 1.6; the long-range anion disorder appears to develop gradually throughout the entire pyrochlore region in contrast to the rapid loss of cation ordering from x = 1.4 to 1.6. The commonly observed two-phase region around the pyrochlore/defect-fluorite phase boundary is absent in this system, demonstrating high sample quality. X-ray absorption near-edge structure (XANES) results at the Y L2-, Ti K- and L3,2-, Hf L3-, and O K-edges indicate a gradual local structural evolution across the whole compositional range; the Y coordination number (CN) decreases and the CN around Ti and Hf increases with increasing Hf content (x). The spectroscopic results suggest that the local disorder occ...