Abstract
Magnets with nominal compositions of (Nd1-x Cex)30 Febal Cu0.1 B1 (x = 0, 0.15, 0.3 and 0.4, mass %) have been fabricated by blending powder method. The remanence (Br), intrinsic coercivity (Hc) and maximum energy product (BH)max of the RE2Fe14B type magnets deteriorated when Nd was replaced by Ce. The chemical composition and crystal structure of magnet were investigated systemically. Backscattered electron (BSE) and energy dispersive spectroscopy (EDS) results revealed that Ce-rich and Ce-lean matrix grains coexisted in the magnets. The magnetic coupling mechanism among the double hard magnetic phases was discussed. Low melting point RE-Cu phase was in favor of the formation of uniform continuous grain boundary. Transmission electron microscopy (TEM) investigation showed the presence of fcc (Nd, Ce)Ox phase in the grain boundary. When the Ce content was 15% of the total amounts of all the rare earth, the maximum energy product of the sintered magnet was 359.8 kJ/m3.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.