Preparation of novel ceramics with high CaO content from steel slag

Abstract

Steel slag, an industrial waste discharged from steelmaking process, cannot be extensively used in traditional aluminosilicate based ceramics manufacturing for its high content of calcium oxide. In order to efficiently utilize such solid waste, a method of preparing ceramics with high CaO content was put forward. In this paper, steel slag in combination with quartz, talcum, clay and feldspar was converted to a novel ceramic by traditional ceramic process. The sintering mechanism, microstructure and performances were studied by scanning electron microscope (SEM), X-ray diffraction (XRD) techniques, combined experimenting of linear shrinkage, water absorption and flexural strength. The results revealed that all crystal phases in the novel ceramic were pyroxene group minerals, including diopsite ferrian, augite and diopsite. Almost all raw materials including quartz joined the reaction and transformed into pyroxene or glass phase in the sintering process, and different kinds of clays and feldspars had no impact on the final crystal phases. Flexural strength of the ceramic containing 40wt.% steel slag in raw materials can reach 143MPa at sintering temperature of 1210°C and its corresponding water absorption, weight loss, linear shrinkage were 0.02%, 8.8%, 6.0% respectively. Pyroxene group minerals in ceramics would contribute to the excellent physical and mechanical properties.