Abstract
ABSTRACT Nitrate-selective, porous magnetic anion-exchange resin (NS-PMAER) with enhanced affinity and higher selectivity for nitrate was synthesized, characterized and its performance in nitrate removal was investigated. The results show that NS-PMAER consists of spherical particles with an average size of 200 μm. It has mean pore diameter, total pore volume, and BET specific surface area of 21.38 nm, 0.3605 cm3/g, and 67.455 m2/g, respectively. The specific saturation magnetization of NS-PMAER was about 10.79 emu/g. Fourier transform infrared spectrometer (FTIR) and X-ray photoelectron spectroscopy (XPS) results indicate that NS-PMAER has selectivity for nitrate higher than that of MIEX® resin; its coefficients of selectivity toward nitrate for nitrate and sulfate are 20.978 and 6.769, respectively, higher than those of MIEX® resin (1.256 and 4.342, respectively). Its working exchange capacity was 72.41 mg/mL. Column-exchange experiments’ results suggest that it could be easily regenerated using 1.5 mol/L sodium chloride solution for a contact time of 30 min. Its recovery rate stayed at > 95% even after five rounds of recycling. Results of the pilot test indicate that NS-PMAER could effectively remove nitrate in groundwater, and ensure that nitrate concentrations of effluent to meet the guideline limit for drinking water by the World Health Organization.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.