Abstract
Using flax stem and ferrous sulfate, a composite porous carbon material was prepared by means of high‐temperature roasting and a one‐step process in a muffle furnace. The samples were characterized using X‐Ray diffraction (XRD) and Scanning electron microscopy (SEM), and the effects of ferrous sulfate concentration, carbonization temperature, and pH values of Cr(VI) aqueous solution on the removal performance of Cr(VI) were studied. XRD and SEM analysis showed that the prepared samples were amorphous porous carbon loaded with FeS/Fe2O3/Fe3O4. High FeSO4 impregnation concentration, high carbonization temperature, and a low pH value of Cr(VI) aqueous solution were beneficial for Cr(VI) removal. When pH = 2, the amount of Cr(VI) removal was 99.93 mg/g by the sample obtained from 1 g flax powder impregnated in 4.5 mmol FeSO4/40 mL H2O solution and calcined for 2 hr at 800°C.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.