Abstract
The 8 wt.% yttria-stabilized zirconia (8YSZ) thermal barrier coatings (TBCs) are widely used to protect hot superalloy components of gas turbine and jet engine. However, Cracks and pores in the 8YSZ coating would accelerate the oxidation of the bondcoat alloy and the corrosion of 8YSZ topcoat by molten salts and finally result in permanent failure of the TBCs. Hence, in this work, a sol-gel spin-coating method was employed to prepare a dense α-Al2O3 film on the surface of air-plasma-sprayed 8YSZ coatings, in order to block the paths of cracks and pores while keeping the stress tolerance of 8YSZ coatings. The influences of the polyvinylpyrrolidone (PVP) and alumina content of the sol on the microstructure of the α-Al2O3 film were investigated. It is found that a sol with PVP addition amount of 50 mg/mL and alumina solid content of 10% let to the achievement of a compact α-Al2O3 film. The positive results in this work would inspire more efforts to prepare dense films on TBCs and therefore improve their performance under service conditions.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.