Abstract
In the preparation processes of aluminum oxynitride (AlON) powders by carbothermal reduction and nitridation, the homogeneity of mixed raw powders between Al2O3 and C is a critical factor by which the final composition and related properties of AlON transparent ceramic will be decided. In this paper, a silane coupling agent was used as a dispersant to optimize the distribution uniformity of raw material of Al2O3 and C, and the preparation of AlON powder with controllable composition and its distribution is investigated. The results show that the silane dispersant could effectively improve the distribution uniformity of raw material. The silane coupling agent contains functional groups of -SiH3 and -CnH2n+1O. XPS showed that the silane could react with C and Al2O3 to form the Si-C bond and C-Al2O3 bond, respectively. The silane coupling agent provides a connected bridge for raw material powders. When the amount of the silane was 5 wt%, the mixed powder had a great distribution uniformity. The addition of silane coupling agent improved the reactivity of raw materials and decreased the synthesis temperature of AlON. The single-phase AlON powder was obtained after the Al2O3/C mixed powder was kept at 1670 °C for 30 min. Furthermore, the grain size of AlON powder was 100-200 nm with an AlN content of 27.5 mol%. With the increase of holding time to 4 h, the grain size increased to 15 μm, indicating that sintering between particles occurred, which may reduce the sintering activity of the powder.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.