Abstract
The Li2O-Al2O3-TiO2-P2O5 system glass ceramic solid electrolytes were prepared by adding Li3BO3 (LB) frits. The phase composition, microstructure and electrical properties of glass ceramics were investigated by using X-ray diffraction, scanning electron microscopy and AC impedance spectroscopy. The results show that the principal crystalline phase of all glass ceramic samples was LiTi2(PO4)3. The grain sizes of glass ceramic sample increase with the increase of sintering temperature. When the additive amount of LB is 1wt %, the glass ceramic solid electrolyte sintered at 950 oC shows the highest room-temperature ionic conductivity of 1.9×10−4 S.cm−1, which can be expected to be used in solid-state lithium-ion batteries.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.