Abstract
With the industrial development, the energy crisis has become a dreadfully serious problem in the world. Therefore, the development of high-durable phase change materials (PCMs) over 600 ℃ is very important for the high-temperature heat energy storage system. An improved three-step process of micro-encapsulated PCMs (MEPCMs) was proposed in this work, including boehmite-precipitation-thermal oxidation treatment, which are beneficial to disperse the thermal stress during high-temperature cycling and restrain crack propagation due to forming a dense and durable Al2O3 shell. The cross-section structure, the surface morphology, phase compositions, phase change temperature, thermal durability and cycling stability were simultaneously investigated. In addition, boehmite-precipitation treatment was performed in an aqueous solution with different adding amounts of Al(OH)3. The thickness of the Al2O3 shell layer was adjusted by control of the amount of Al(OH)3. The latent heat of the MEPCMs with the adding amount of 2 g/L Al(OH)3 reached 180 J/g, and the released heat was 110 J/g after 100 cycles of melting-solidification. Furthermore, TEM observation further confirmed the formation of θ-Al2O3 crystal structure on the surface, which is helpful to the durability. Every MEPCM kept a completely spherical shape and a dense surface after 100 cycles of melting-solidification. Therefore, the MEPCMs with excellent heat storage capacity and high thermal stability were widely used to recycle industry, such as waste heat, building energy conservation and aerospace. In addition, the new processing technology can provide excellent and industrial production of PCMs in the future.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.