Abstract
A new kind of polytriazole resins were prepared from a triazide and a dialkyne compounds and characterized. These resins can be cured at 80 °C. The curing process for a resin was traced by FT-IR. The glass transition temperature Tg and thermal decomposition temperature Td5 of the cured resin with the molar ratio of azide group to alkyne group [a]/[b]=1.0:1.0 reach 216 °C and 360 °C, respectively. The flexural strength of the cured resin and its glass fiber reinforced composite arrive at 183.6 MPa and 963.4 MPa, respectively. The resin would be a good candidate for the matrices of advanced composites.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.