Abstract

Indium tin oxide (ITO) films were deposited on glass substrates by using the homemade spray pyrolysis system. Orthogonal test was designed to examine the optimal conditions for preparation of the ITO films. The results showed that the ITO thin films can be prepared by the homemade spray pyrolysis device successfully. The device is simple in structure and easy to use. The substrate temperature is the main factor on the photoelectric properties of the ITO films. The optimal conditions for preparing the ITO thin films were as following: the substrate temperature is 300oC, the carrier gas flow of the air was 1.5 L•min-1, the annealing temperature was 500oC, the proportion of the indium and tin was 10:1, the distance between substrate and nozzle was 8 cm, and the deposition time was 3.5 min. The average optical transmittance in the visible range and sheet resistance of the ITO film were 93% and 2786Ω/□, respectively.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.