Abstract
A Hf-doped β-(Ni,Pt)Al coating was prepared by co-deposition of a Pt-Hf composite plating and successive aluminisation. Then, a distinct Hf-rich belt was formed internally between the outer additive (Ni,Pt)Al coating and interdiffusion zone. An isothermal oxidation test at 1100°C revealed a relatively lower oxidation rate constant and decreased oxide scale rumpling tendency for the Hf-doped coating during which the Hf-rich belt partly acted as an effective diffusion barrier. The unique addition of Hf into a β-(Ni,Pt)Al coating can delay the transitional oxidation period from transient alumina to stable one and postpone the degradation from β to γ'.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.