Abstract
A microcrystalline β-NiAl coating was prepared on a single-crystal (SC) superalloy substrate via magnetron sputtering and subsequent vacuum annealing. The grain sizes of the coating ranged from about 300nm to 1μm. A reference NiCrAlY coating, which was mainly comprised of γ′-Ni3Al and α-Cr, was prepared by means of vacuum arc evaporation (VAE). Isothermal oxidation tests were carried out at 1100°C in air for 50h. Both coatings formed thin and adherent α-Al2O3 scales during tests, while the oxide scales on the bare superalloy primarily consisted of spinel (Ni,Co)Al2O4 with underlying α-Al2O3 scale. The parabolic rate constant of the NiAl-coated specimens was about one order of magnitude lower than that of the NiCrAlY coated specimens. After oxidation tests, only a small amount of γ′ phase was detected at some columnar boundaries of the β-NiAl coating, and about 2/3 parts of the NiCrAlY coating transformed into γ phase which resolved the α-Cr precipitations, while an Al-depleted zone in thickness of about 10μm formed beneath the TGO of the bare superalloy. Inter-diffusion zones and secondary reaction zones were observed on the specimens coated by either β-NiAl or NiCrAlY. The oxidation mechanism and microstructure evolvement of the specimens during high temperature exposures were discussed.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.