Abstract
Al–Si base composites reinforced with different mixtures of Ni and nano-Al2O3 particles have been fabricated by squeeze casting and their metallurgical and mechanical characterization has been investigated. A mixture of Ni and nano-Al2O3 particles of different ratios was added to the melted Al–Si piston alloy at 700°C and stirred under pressure. After the Al-base-nano-composites were fabricated by squeeze casting, the microstructure and the particle distribution inside the matrix have been investigated using optical and scanning electron microscopes. Moreover, the hardness and the tensile properties of the resulted Al-base-nano-composites were evaluated at room temperature by using Vickers hardness and universal tensile testers, respectively. As a result, in most cases, it was found that the matrix showed a fine eutectic structure of short silicon constituent which appeared in the form of islands in the α-phase around some added particle agglomerations of the nano-composite structures. The tendency of this structure formation increases with the increase of Ni particle addition. As the ratio of the added particles increases, the tendency of these particles to be agglomerated also increases. Regarding the tensile properties of the fabricated Al-base-nano-composites, ultimate tensile strength is increased by adding the Ni and nano-Al2O3 particles up to 10 and 2wt.%, respectively. Moreover, the ductility of the fabricated composites is significantly improved by increasing the added Ni particles. The composite material reinforced with 5wt.% Ni and 2wt.% nano-Al2O3 particles showed superior ultimate tensile strength and good ductility compared with any other added particles in this investigation.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: Journal of King Saud University - Engineering Sciences
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.