Abstract
In this paper the preparation of two sets of polycrystalline photocatalysts prepared by supporting TiO 2 (anatase) on TiO 2 (rutile) or Al 2O 3 is reported. The powders were prepared by a wet impregnation method using titanium(IV) isopropylate. The impregnation was followed by thermal treatment and this procedure was repeated several times in order to obtain samples with progressively increasing amounts of TiO 2 (anatase). The photocatalytic activity of all of the specimens was tested by carrying out the 4-nitrophenol photodegradation, used as a “probe” reaction, in aqueous medium and in different kinds of batch photoreactors. The solids were characterised by X-ray diffraction (XRD), specific surface area (BET) and porosity determination, scanning electron microscopy observation (SEM) coupled with energy dispersive X-ray analysis (EDX), visible–ultraviolet diffuse reflectance spectroscopy (DRS) and Fourier transform infrared spectroscopy (FTIR) monitoring of surface acidity. The characterisation results indicate an increase of TiO 2 anatase phase with the number of impregnations. The porosity and the surface area of all the photocatalysts prepared by supporting TiO 2 (anatase) on TiO 2 (rutile) were always higher than that of the bare support, while those of the samples prepared by supporting TiO 2 (anatase) on Al 2O 3 were lower than that of bare Al 2O 3. The FTIR measurements indicated that Lewis acid sites (Ti 4+ or both Ti 4+ and Al 3+) were present on the surface of the two sets of supported samples, while no Brønsted acid sites were detected. The preparation method used allowed to obtain samples quite resistant to disaggregation when they were mixed in water. Moreover they showed to be easily decantable after the occurrence of the runs. Both sets of TiO 2 (anatase) supported samples resulted photoactive and the photoactivity increased by increasing the content of the anatase phase, although it was less significant than that of a pure home prepared and Degussa P25 TiO 2 samples, tested for the sake of comparison.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.