Abstract
The precipitation orientation of α phases in a Ti-55511 alloy during the heat treatment and the subsequent hot deformation is investigated. It is observed that the β grains prominently influence the precipitation process of α phases, i.e., for the neighbouring β grains without similar {110} pole, the precipitation orientation of grain boundary (GB) α phases (αGB) keep {0001}//{110}β1 or {0001}//{110}β2 to maintain the burgers orientation relationship (BOR) with the neighbouring β grains. For the neighbouring β grains with similar {110} pole, the {0001} poles of αGB phases precipitate parallel to this similar {110} pole and maintain BOR with the neighbouring β grains. For the neighbouring β grains with multiple similar {110} poles, the {0001} poles of αGB phases precipitate along these similar poles and maintain BOR with the neighbouring β grains. Besides, the interface instability nucleation and sympathetic nucleation are the main nucleation modes of the GB widmanstatten α phase (αWGB), which primarily precipitate within β grains with the similar orientation of αGB phases. The intracrystalline widmanstatten phase (αWI) precipitate in a single β grain with 12 precipitation orientations. The BOR between αWI phases and β grains is destroyed during the subsequent hot compressive deformation.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.