Powder Synthesis and Characterization of Al0.5CoCrFeNi High-Entropy Alloy for Additive Manufacturing Prepared by the Plasma Rotating Electrode Process.

Abstract

The Al0.5CoCrFeNi high-entropy alloy powder was produced by using a plasma rotating electrode process. The morphology, microstructure, and physical properties of the powder were characterized. The powder exhibited a smooth surface and a narrow particle size distribution with a single peak. The relationships between particle size and secondary dendrite arm space as well as cooling rate were evaluated as follows: λ = 0.0105d + 0.062 and vc = 4.34 × 10-5d-2 + 2.62 × 10-2d-3/2, respectively. The Al0.5CoCrFeNi powder mainly consisted of fcc + bcc phases. As the powder particle size decreased, the microstructure of the powder changed from dendritic to columnar or equiaxed, along with a decrease in the fcc content and an increase in the bcc content. The tap density (4.76 g cm-3), flowability (15.01 s × 50 g-1), oxygen content (<300 ppm), and sphericity (>94%) of the powder indicated suitability for additive manufacturing.