Abstract
In this study, rapidly solidified metal matrix composite powders have been produced by PREP (Plasma rotating electrode process) atomization. AlCu4Mg1 alloy is used as the matrix material while SiC particles, with about 650 nm average particle size, are used as the reinforcement phase. The microstructural and solidification characteristics of composite particles are studied using optical and scanning electron microscope (SEM). The relationship between secondary dendrite arm spacing (SDAS) and particle diameter was examined, and these composite powders were found to have dendritic and equiaxed solidification with a fine eutectic phase. SDAS measurements using various sized particles show that secondary dendrite arm spacing slightly decreases with the decrease in particle size.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of Mining and Metallurgy, Section B: Metallurgy
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.