Potential and Design Parameters of Polyvinylidene Fluoride in Gear Applications.

Abstract

(1) Background: With the ever-increasing number of polymer materials and limited data on polymer gear calculations, designers are often required to perform extensive experimental testing in order to establish reliable operational data for specific gear applications. This research investigates the potential of a Polyvinyldene fluoride (PVDF) polymer material in gear applications, considering various loading conditions and different types of gear transmission configurations, including both self-mated mesh and steel/PVDF mesh. (2) Methods: PVDF gear samples were tested on a specially designed test rig that enables active torque control and temperature monitoring in order to obtain the necessary design parameters and failure modes. Each test for certain load conditions was repeated five times, and to fully investigate the potential of PVDF gear samples, comparative testing was performed for Polyoxymethylene (POM) gear. (3) Results: Tribological compatibility, tooth load capacity, and lifespan assessment, along with the types of failure, which, for some configurations, include several types of failures, such as wear and melting, were determined. Temperature monitoring data were used to estimate the coefficient of friction at the tooth contact of analyzed gear pairs, while optical methods were used to determine a wear coefficient. (4) Conclusions: The tribological compatibility of polymer gear pairs needs to be established in order to design a gear pair for a specific application. PVDF gear samples mated with steel gear showed similar lifespan properties compared to POM samples. Temperature monitoring and optical methods serve as a basis for the determination of the design parameters. PVDF is an appropriate material to use in gear applications, considering its comparable properties with POM. The particular significance of this research is reflected in the establishment of the design parameters of PVDF gear, as well as in the analysis of the potential of the PVDF material in gear applications, which gives exceptional significance to the current knowledge on polymer gears, considering that the PVDF material has not previously been analyzed in gear applications.