Abstract
Titanium-containing mesoporous silica TiO2/MCM-41 (C) was prepared by impregnating MCM-41, pretreated by refrigeration at 278K, with aqueous TiCl4 solution as titanium precursor. In addition, TiO2/MCM-41 (H) was produced by same method but the support MCM-41 without refrigeration in order to investigate the influence of unrefrigerated pretreatment on the structure of TiO2/MCM-41. The dispersion and nature of titanium species were characterized by inductively coupled plasma mass spectrometry (ICP-MS), powder X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR), UV–visible diffuse reflectance spectra (UV-vis DRS), standard Brunauer–Emmnett–Teller (BET), X-ray photoelectron spectra (XPS), scanning electron micrographs (SEM), transmission electron microscopy (TEM). The results indicate that TiO2/MCM-41 (C) showed better mesoscopic order, higher dispersion of titanium oxide species, stronger interaction with the MCM-41 support. But the pore size decreases from 3.4 to 2.4nm when the titanium content increases to 76.6mg/g. TiO2/MCM-41 (C2) exhibits more excellent catalytic performance than others, and the 97.6% conversion of methyl oleate (MO) and 93.1% selectivity to epoxidation methyl oleate (EMO) can be obtained at 353K for 10h.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.